Ultramid® 1503-2 BK ND3007 | PA66-GF33 | BASF
材料文字说明
Ultramid® 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.
机械性能干 / 已调节单位测试标准
拉伸模量10800 / -MPaISO 527-1/-2
断裂应力190 / 144MPaISO 527-1/-2
断裂伸长率3 / 5%ISO 527-1/-2
简支梁缺口冲击强度, +23°C11 / -kJ/m²ISO 179/1eA
简支梁缺口冲击强度, -30°C8 / -kJ/m²ISO 179/1eA
热性能干 / 已调节单位测试标准
熔融温度, 10°C/min257 / *°CISO 11357-1/-3
热变形温度, 1.80 MPa255 / *°CISO 75-1/-2
热变形温度, 0.45 MPa264 / *°CISO 75-1/-2
其它性能干 / 已调节单位测试标准
吸水性5.7 / *%类似ISO 62
吸湿性1.7 / *%类似ISO 62
密度1400 / -kg/m³ISO 1183
函数
www.campusplastics.com02468050100150200250应力-应变.Ultramid® 1503-2 BK ND3007 (干)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com01234567050100150应力-应变.Ultramid® 1503-2 BK ND3007 (湿)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com02468020004000600080001000012000正割模量-应变.Ultramid® 1503-2 BK ND3007 (干)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com0123456710002000300040005000600070008000正割模量-应变.Ultramid® 1503-2 BK ND3007 (湿)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
典型数据