Lexan PC 945物性


非填充,注射级,无氯,非溴UL - 94 V0,有各种不透明的颜色,适用范围广


Property

TYPICAL PROPERTIES (1)
MECHANICAL
ValueUnitStandard
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm2
ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min
660
kgf/cm2
ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min
6
%
ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min
125
%
ASTM D 638

Tensile Modulus, 50 mm/min
23200
kgf/cm2
ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span
1030
kgf/cm2
ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span
23900
kgf/cm2
ASTM D 790

IMPACT
ValueUnitStandard
Izod Impact, notched, 23°C
81
cm-kgf/cm
ASTM D 256

Instrumented Impact Total Energy, 23°C
748
cm-kgf
ASTM D 3763

THERMAL
ValueUnitStandard
Vicat Softening Temp, Rate B/50
143
°C
ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed
137
°C
ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed
126
°C
ASTM D 648

CTE, -40°C to 40°C, flow
6.66E-05
1/°C
ASTM E 831

CTE, -40°C to 40°C, xflow
6.66E-05
1/°C
ASTM E 831

Relative Temp Index, Elec
130
°C
UL 746B

Relative Temp Index, Mech w/impact
120
°C
UL 746B

Relative Temp Index, Mech w/o impact
130
°C
UL 746B

PHYSICAL
ValueUnitStandard
Specific Gravity
1.19
-
ASTM D 792

Mold Shrinkage, flow, 3.2 mm
0.6 - 0.8
%
SABIC Method

Melt Flow Rate, 300°C/1.2 kgf
10
g/10 min
ASTM D 1238

ELECTRICAL
ValueUnitStandard
Arc Resistance, Tungsten {PLC}
7
PLC Code
ASTM D 495

Hot Wire Ignition {PLC)
2
PLC Code
UL 746A

High Voltage Arc Track Rate {PLC}
4
PLC Code
UL 746A

High Ampere Arc Ign, surface {PLC}
3
PLC Code
UL 746A

Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A

FLAME CHARACTERISTICS
ValueUnitStandard
UL Recognized, 94V-2 Flame Class Rating (3)
0.8
mm
UL 94

UL Recognized, 94V-0 Flame Class Rating (3)
1.14
mm
UL 94

UL Recognized, 94-5VA Rating (3)
3.04
mm
UL 94

Glow Wire Flammability Index 960°C, passes at
1
mm
IEC 60695-2-12

Glow Wire Ignitability Temperature, 1.0 mm
875
°C
IEC 60695-2-13

Oxygen Index (LOI)
35
%
ISO 4589

Processing
Parameter
Injection Molding
ValueUnit
Drying Temperature
120
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
48
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
295 - 315
°C
Nozzle Temperature
290 - 310
°C
Front - Zone 3 Temperature
295 - 315
°C
Middle - Zone 2 Temperature
280 - 305
°C
Rear - Zone 1 Temperature
270 - 295
°C
Mold Temperature
70 - 95
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
40 - 60
%
Vent Depth
0.025 - 0.076
mm

耐高温PC、耐寒PC、增强PC、注塑级PC、食品级PC

沙伯基础(原美国GE)LEXAN系列聚碳酸酯PC

PC:121R-111、141R-111、101R-111、注塑级、易脱模

PC:123R、143R、103R、133R、153R、抗紫外线

PC:124R、144R、104R、134R、食品级聚碳酸酯

PC:920、940、950阻燃级、不透明。

PC:940A、920A、950A透明阻燃级

PC:500R、503R阻燃V0、GF10

PC:3412R、3432R、阻燃V1、GF20

PC:3413R、3433R阻燃V1、GF30

PC:3414R、阻燃V1、GF40

PC:LS1、LS2、LS3、光学级、汽车灯用

PC:HF1110、HF1110R、HF1140、高流动级。

PC:EXL1414、增韧耐寒级

聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物,根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低,从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获的了工业化生产。聚碳酸酯无色透明,耐热,抗冲击,阻燃BI级,在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比,聚碳酸酯的耐冲击性能好,折射率高,加工性能好,不需要添加剂就具有UL94 V-0级阻燃性能。聚碳酸酯的应用开发是向高复合、高功能、专用化、系列化方向发展,目前已推出了光盘、汽车、办公设备、箱体、包装、医药、照明、薄膜等多种产品各自专用的品级牌号。


LEXAN由双酚A制造,为聚碳酸脂高分子材料,具有优异的高透明和耐热温度,以及热可塑性树脂中最高的冲击强度,良好的成型性使得“LEXAN”用于汽车零组件、事务机器、家电产品、电子产品、电子零件、食品器具、医疗器材和通信设备之替代金属用品上,最佳的选择材料。

东莞市远翔工程塑胶原料有限公司为您提供详细的Lexan PC 943物性表参数。如果您对我们的Lexan PC 943有任何疑问,或者想索取Lexan PC 943 物性表、物质安全资料证书MSDS、ROHS检验报告、SGS报告、REACH环保证明、FDA证明、EU法规证明、UL证书及出厂证明COC/COA报告等,敬请拨打我们的服务热线0769-86992218,或者给我们留言。


会员登录
登录
我的资料
我的收藏
留言
回到顶部